Bambu Lab TPU 95A HF Filament 1.75mm
Bambu Lab TPU 95A HF is an optimized TPU filament designed specifically for high-speed 3D printing. Unlike regular TPU 95A, this variant offers an impressive 3x faster printing speed. As a result, it effectively addresses the common problem of lengthy print times associated with other TPU filaments. Moreover, TPU 95A HF retains all the key advantages of traditional TPU, including exceptional interlayer adhesion, impact resistance, flexibility, and resilience at low temperatures. Therefore, you can experience faster TPU printing without sacrificing quality or performance.
High Speed Printing
Elevate your TPU printing efficiency to the next level with Bambu TPU 95A HF, featuring a print speed that's 3 times faster than standard TPU 95A.
| Bambu TPU 95A | Bambu TPU 95A HF | |
| Nozzle Temperature / °C | 230 | 230 |
| Max Volumetric Speed / (mm³/s) | 3.6 | 12 |
| Printing Speed / (mm/s) | 44 | 147 |
| Model Specimens | Diameter: 50 mm Height: 100 mm Infill:40% | |
Soft and Flexible
Bambu TPU HF is an exceptionally soft and flexible filament with extraordinary impact resistance, enabling you to print parts that need withstand impact, collision, and falling.
Widely Used Application
Accessory Compatibility
| Recommended | Not Recommended | |
| Build Plate |
Smooth PEI Plate, Textured PEI Plate
|
Cool Plate SuperTack
|
| Hotend |
Hotend with Hardened Steel Nozzle 0.4 mm / 0.6 mm / 0.8 mm
Hotend with Stainless Steel Nozzle 0.4 mm
|
Hotend with Hardened Steel Nozzle 0.2 mm
Hotend with Stainless Steel Nozzle 0.2 mm
|
| Glue | Bambu Liquid Glue Glue Stick |
/ |
| Recommended Printing Settings | |
| Drying Settings (Blast Drying Oven) | 70 °C，8 h |
| Printing and Keeping Container's Humidity | < 20% RH (Sealed, with Desiccant) |
| Nozzle Temperature | 220 - 240 °C |
| Bed Temperature (with Glue) | 30 - 35 °C |
| Printing Speed | < 200 mm/s |
| Physical Properties | |
| Density | 1.22 g/cm³ |
| Vicat Softening Temperature | N / A |
| Heat Deflection Temperature | N / A |
| Melting Temperature | 183 °C |
| Melt Index | 36.5 ± 2.6 g/10 min |
| Mechanical Properties | |
| Tensile Strength | 27.3 ± 0.8 MPa |
| Breaking Elongation Rate | > 650% |
| Bending Modulus | N / A |
| Bending Strength | N / A |
| Impact Strength | N / A |